This study investigates the effect of interlayer temperature control and post-processing heat treatments on the microstructure and hardness of modified PH 13-8 Mo manufactured using directed energy deposition with a laser beam and powder (DED-LB/p). Modified PH 13-8 Mo blocks were deposited at controlled interlayer temperatures. By controlling the interlayer temperature (180 ± 5 °C) above the Ms temperature, a relatively homogeneous microstructure and hardness (344 ± 7 HV0.2) were achieved in the as-deposited material. The average hardness of the depositions increased to 366 ± 15 HV0.2 and 397 ± 32 HV0.2 as interlayer temperatures (100 ± 5 °C and 30 ± 5 °C) decreased below the Ms temperature, accompanied by a transition from a more homogeneous to a heterogeneous microstructure, driven by the intrinsic heat treatment during deposition. Additionally, the blocks were subjected to post-processing solution heat treatment, which reduced microstructural variations, leading to comparable hardness values regardless of interlayer temperature. The highest average hardness (528 HV0.2) across all interlayer temperatures was achieved after solution heat treatment followed by aging. These findings highlight the potential and effectiveness of interlayer temperature control and post-processing heat treatments to tailor the microstructure and hardness of modified PH 13-8 Mo manufactured by DED-LB/p

Effective thermal management is essential in metal additive manufacturing to ensure process stability and desirable material properties. Directed energy deposition using a laserbeam and wire (DED-LB/w) enables the production of large, high-performance components but remains sensitive to adverse thermal effects during multilayer deposition due to heat accumulation. While prior studies have investigated interlayer temperature control and substrate preheating in DED modalities, including laser-powder and arc-based systems, the influence of substrate preheating in DED-LB/w has not been thoroughly examined.

This study employs substrate preheating to simulate heat accumulation and assess its effects on melt pool geometry, wire–melt pool interaction, and the microstructural evolution of Alloy 718. Experimental results demonstrate that increased substrate temperatures lead to a gradual expansion of the melt pool, with a notable transition occurring beyond 400 ◦C. Microstructural analysis reveals that elevated preheat temperatures promote coarser secondary dendrite arm spacing and the development of wider columnar grains. Moreover, Nb-rich secondary phases, including the Laves phase, exhibit increased size but relatively unchanged area fractions. Observations from electrical conductance measurements and coaxial visual imaging show that preheat temperature significantly affects the process dynamics and microstructural evolution, providing a basis for advanced process control strategies.

The PH 13-8 Mo family of steels belong to the martensitic precipitation hardening stainless steels (MPHSSs) category, which exhibits a good combination of mechanical properties and corrosion resistance. Additive manufacturing (AM) offers advantages, including reduced material waste and the capability to produce complex, near-net-shape parts. Consequently, the application of AM techniques to the PH 13-8 Mo family is being increasingly explored across various industries. This review paper presents the existing literature on the topic and provides an overview. The review starts by presenting information about the PH 13-8 Mo family, including microstructure, chemical compositions, heat treatments, and mechanical properties. Afterwards, the work focuses on presenting the microstructure and resulting properties of PH 13-8 Mo family processed by three different additive manufacturing processes: Powder Bed Fusion using a Laser Beam (PBF-LB), Directed Energy Deposition using an Electric Arc (DED-Arc), and Directed Energy Deposition using a Laser Beam (DED-LB), both in their as-built condition and following post-processing heat treatments. The review concludes with a summary and outlook that highlights existing knowledge gaps and underscores the need for further research to tailor the microstructural evolution and enhance the properties. The findings indicate that AM of the PH 13-8 Mo family has the potential for industrial applications, yet further studies are necessary to optimize its performance.

The combination of corrosion resistance and mechanical properties of martensitic precipitation hardening stainless steels (MPHSS) makes them well suited for demanding applications in aerospace, high-pressure gas bottles, or in injection molding of corrosive plastics. Directed energy deposition methods and specifically the laser metal deposition process with powder as feedstock (LMDp) have the potential to be applied in the production of such components. It is well-known that the geometrical features of the deposited beads such as aspect ratio and dilution are crucial for process efficiency and deposition quality. Therefore, this work aims at understanding the influence of the process parameters and the resulting microstructure of a MPHSS modified PH 13-8Mo alloy when using LMDp. Design of experiment (DoE) was used to plan and analyze the influence and interaction of the different LMDp process variables in the geometry of the deposits. It was found that height, width, and depth were statistically significantly influenced by speed, while height was also considerably influenced by the powder feeding rate. In terms of laser power, it was the most significant factor for the width and the depth, but it did not significantly affect the height of the beads. The results showed that the as-deposited microstructure of the modified PH 13-8Mo under the LMDp conditions investigated in this work consists of a martensitic matrix with some amount of primary δ ferrite. The presence of a low amount of retained austenite and aluminum-enriched inclusions was confirmed. This work enhances the fundamental process and material understanding of LMDp of the modified PH 13-8Mo alloy as a first stage in the fabrication of additively manufactured components.

Modified PH 13-8Mo alloy exhibits a good combination of corrosion resistance and mechanical properties for demanding applications in aerospace, petrochemical, and tooling industries. Additive manufacturing, specifically the laser metal deposition process with powder as feedstock (LMDp), has the potential to be utilized in these industries. However, very limited knowledge on the LMDp of this alloy currently exists. The aim of this work was, therefore, to deposit a multi-track single layer of modified PH 13-8Mo alloy as a first step towards 3D geometries, and to analyze the resulting microstructure by using Optical Microscopy, Scanning Electron Microscopy, X-Ray Diffraction, Electron Backscatter Diffraction, and micro-hardness. It was found that the multitrack single layer was free from major defects. The microstructure was heterogeneous, and it consisted of a martensitic matrix and small amounts of δ ferrite, austenite, and AlN. The results of this research will be used to tailor the microstructure and properties of future 3D additively manufactured components.