Microstructure and mechanical properties of low-temperature hot isostatic pressed Ti-6Al-4V manufactured by electron beam melting
University West, Department of Engineering Science, Division of Subtractive and Additive Manufacturing. (PTW)
2022 (English)Licentiate thesis, comprehensive summary (Other academic)
Abstract [en]

Ti-6Al-4V manufactured by electron beam melting Keywords: Additive manufacturing, high-temperature tensile properties, low cycle fatigue, neutron diffraction, fatigue crack growth ISBN: 978-91-89325-27-2 (Printed) 978-91-89325-26-5 (Electronic) Ti-6Al-4V is the most widely used α+β titanium alloy in aerospace engine applications due to its high specific strength. Typically, the alloy is manufactured as castings or forgings and then machined to final geometry. These conventional manufacturing processes do however generate a lot of waste material, whereas additive manufacturing (AM) can potentially produce a near-net-shape geometry directly from the feedstock. In the past decade, electron beam melting (EBM), one of the powder bed fusion techniques, has been widely researched to build Ti[1]6Al-4V components. Still, the as-built material can contain defects such as gas pores that require post-processing, such as hot isostatic pressing (HIP) to produce nearly fully dense components. HIP treatment of conventionally cast Ti-6Al-4V is normally performed at 920 ˚C, 100 MPa for 2 hours. This same HIP treatment has then been adapted also for EBM-manufactured Ti-6Al-4V, which however results in coarsening of α laths and reduction of yield strength. Therefore, finding a more appropriate HIP treatment for this new type of Ti-6Al-4V material, i.e. EBM manufactured, would be of great benefit for the industry. Lowering the HIP treatment temperature to 800 ˚C and increasing the pressure to 200 MPa has recently been proven to close the porosity to a high degree while sustaining the high yield strength. In this thesis, the high-temperature tensile properties of EBM-manufactured Ti[1]6Al-4V subjected to a low-temperature (800 ˚C) HIP treatment were evaluated and compared with standard HIP-treated (920 ˚C) materials. Metallurgical characterization of the as-built, HIP-treated materials have been carried out to understand the effect of temperature on the microstructures. The standard HIP[1]treated material measured about 1.4x - 1.7x wider α laths than those in the low[1]temperature HIP treated and as-built samples, respectively. The standard HIP[1]treated material showed about 10 - 14% lower yield strength than other HIP treated materials. At 350 ˚C the yield strength decreases to about 65% compared to the room temperature strength for all tested materials. An increase in ductility vi programvaran NASGRO där livsförutsägelserna visade god överensstämmelse med experimentella livscykler i de flesta fall. vii Abstract Title: Microstructure and mechanical properties of low-temperature hot isostatic pressed Ti-6Al-4V manufactured by electron beam melting Keywords: Additive manufacturing, high-temperature tensile properties, low cycle fatigue, neutron diffraction, fatigue crack growth ISBN: 978-91-89325-27-2 (Printed) 978-91-89325-26-5 (Electronic) Ti-6Al-4V is the most widely used α+β titanium alloy in aerospace engine applications due to its high specific strength. Typically, the alloy is manufactured as castings or forgings and then machined to final geometry. These conventional manufacturing processes do however generate a lot of waste material, whereas additive manufacturing (AM) can potentially produce a near-net-shape geometry directly from the feedstock. In the past decade, electron beam melting (EBM), one of the powder bed fusion techniques, has been widely researched to build Ti[1]6Al-4V components. Still, the as-built material can contain defects such as gas pores that require post-processing, such as hot isostatic pressing (HIP) to produce nearly fully dense components. HIP treatment of conventionally cast Ti-6Al-4V is normally performed at 920 ˚C, 100 MPa for 2 hours. This same HIP treatment has then been adapted also for EBM-manufactured Ti-6Al-4V, which however results in coarsening of α laths and reduction of yield strength. Therefore, finding a more appropriate HIP treatment for this new type of Ti-6Al-4V material, i.e. EBM manufactured, would be of great benefit for the industry. Lowering the HIP treatment temperature to 800 ˚C and increasing the pressure to 200 MPa has recently been proven to close the porosity to a high degree while sustaining the high yield strength. In this thesis, the high-temperature tensile properties of EBM-manufactured Ti[1]6Al-4V subjected to a low-temperature (800 ˚C) HIP treatment were evaluated and compared with standard HIP-treated (920 ˚C) materials. Metallurgical characterization of the as-built, HIP-treated materials have been carried out to understand the effect of temperature on the microstructures. The standard HIP[1]treated material measured about 1.4x - 1.7x wider α laths than those in the low[1]temperature HIP treated and as-built samples, respectively. The standard HIP[1]treated material showed about 10 - 14% lower yield strength than other HIP treated materials. At 350 ˚C the yield strength decreases to about 65% compared to the room temperature strength for all tested materials. An increase in ductility viii was observed at 150 ˚C compared to that at room temperature, but the ductility decreased between 150 - 350 ˚C because of activation of different slip systems. The low cycle fatigue (LCF) behavior of such a modified HIP (low-temperature HIP) material is assessed at two different strain levels and compared with the corresponding LCF properties for the standard HIP material. Even though the modified HIP material had lowest minimum life cycles to failure, the overall fatigue performance is comparable with that of the standard HIP material. Also, fatigue life predictions were made from the measured defect size at the crack initiation site using NASGRO. The calculated life predictions showed good agreement with the experimental values in most cases. In-situ neutron diffraction measurements on tensile test specimens were conducted, at both room temperature and at 350˚ C, for the standard and modified HIP-treated materials. The objective was to gain essential insights on how the crystal lattice strains relate to the macroscopic strengths in these specific microstructures. This investigation helped to understand the load partitioning between different slip planes and constituent phases in the microstructure at different temperatures.

Abstract [sv]

Ti-6Al-4V är den mest använda α+β titanlegeringen i flygmotortillämpningar på grund av sin höga specifika hållfasthet. Vanligtvis tillverkas legeringen som gjutgods eller smide och bearbetas sedan till slutlig geometri. Dessa konventionella tillverkningsprocesser genererar dock en hel del avfallsmaterial, medan additiv tillverkning (AM) potentiellt kan producera en nästan slutgiltlig geometri direkt från råvaran. Under det senaste decenniet har elektronstrålesmältning (EBM), en av pulverbäddsfusionsteknikerna, undersökts mycket för att bygga Ti-6Al-4V-komponenter. Ändå kan det byggda materialet innehålla defekter såsom gasporer som kräver efterbearbetning, såsom varm isostatisk pressning (HIP) för att producera nästan helt täta komponenter. HIP[1]behandling av konventionellt gjutet Ti-6Al-4V utförs normalt vid 920 ˚C, 100 MPa under 2 timmar. Samma HIP-behandling har sedan anpassats även för EBM[1]tillverkat Ti-6Al-4V, vilket dock resulterar i förgrovning av α-lameller och minskning av sträckgränsen. Att hitta en mer lämplig HIP-behandling för denna nya typ av Ti-6Al-4V-material, dvs EBM-tillverkat, skulle därför vara till stor fördel för industrin. Att sänka HIP-behandlingstemperaturen till 800 ˚C och öka trycket till 200 MPa har nyligen visat sig stänga porositeten i hög grad samtidigt som den höga sträckgränsen bibehålls. Ti-6Al-4V används huvudsakligen i applikationer för flygmotorer upp till en maximal driftstemperatur på 300 ˚C. Därför studerades högtemperaturdragegenskaperna hos de olika HIP-behandlade EBM[1]byggmaterialen i detta forskningsarbete. Denna studie visade att duktiliteten påverkas av aktiveringen av olika glidsystem baserat på temperatur. Ytterligare neutrondiffraktionsexperiment utfördes tillsammans med in-situ dragprovning för att bestämma det aktiva glidsystemet vid en specifik temperatur. Utmattningsbeteendet hos det lågtemperaturbehandlade HIP-materialet utvärderas också genom lågcykelutmattningstestning och utmattningsspricktillväxttest. Utmattningsprestandan för det modifierade HIP[1]materialet utvärderades mot standard HIP- material och visade sig ha jämförbara utmattningsegenskaper. Förutsägelser om utmattningsliv utfördes med hjälp av vi programvaran NASGRO där livsförutsägelserna visade god överensstämmelse med experimentella livscykler i de flesta fall. 

Place, publisher, year, edition, pages
Trollhättan: University West , 2022. , p. 67
Series
Licentiate Thesis: University West ; 39
Keywords [en]
Additive manufacturing, high-temperature tensile properties, low cycle fatigue, neutron diffraction, fatigue crack growth
Keywords [sv]
Additiv tillverkning, dragprovning vid hög temperatur, låg cykelutmattning, neutrondiffraktion, tillväxt av utmattningssprickor
National Category
Manufacturing, Surface and Joining Technology
Research subject
Production Technology
Identifiers
URN: urn:nbn:se:hv:diva-18401ISBN: 978-91-89325-27-2 (print)ISBN: 978-91-89325-26-5 (electronic)OAI: oai:DiVA.org:hv-18401DiVA, id: diva2:1660490
Presentation
2022-06-15, 111, Gustava Melins gata, Trollhättan, 10:00 (English)
Opponent
Supervisors
Note

Submitted papers or manuscripts have been excluded from the fulltext file.

Available from: 2022-06-15 Created: 2022-05-24 Last updated: 2022-06-22Bibliographically approved

Open Access in DiVA

fulltext(3198 kB)313 downloads
File information
File name FULLTEXT01.pdfFile size 3198 kBChecksum SHA-512
c02a35091395756c8caf24fe34427fa57316ff048fd3c24eac8e0ca90fa09cb6c3caaaad3399ac9c53841534c169d7180436df14ea65707b042ba6ce7c2ae592
Type fulltextMimetype application/pdf
fulltext(104 kB)49 downloads
File information
File name FULLTEXT03.pdfFile size 104 kBChecksum SHA-512
429de731d24ee3204b2640ed82e19b2150ecf8229a91ccf05bb811c673103ef026ccfea72d05d52d530cc4314c1450cc5d5480e07d2e921588a2689c5d25a352
Type fulltextMimetype application/pdf
fulltext(110 kB)54 downloads
File information
File name FULLTEXT06.pdfFile size 110 kBChecksum SHA-512
f8a3543d40338c0c6701d1f67c4a15798fbaf5114f20eca1cea4bced47055123f9261ec9ea49a5b974271b62f7d369d5b5624cfadf55dd45e49a287481ae14a4
Type fulltextMimetype application/pdf

Authority records

Thalavai Pandian, Karthikeyan

Search in DiVA

By author/editor
Thalavai Pandian, Karthikeyan
By organisation
Division of Subtractive and Additive Manufacturing
Manufacturing, Surface and Joining Technology

Search outside of DiVA

GoogleGoogle Scholar
Total: 418 downloads
The number of downloads is the sum of all downloads of full texts. It may include eg previous versions that are now no longer available

isbn
urn-nbn

Altmetric score

isbn
urn-nbn
Total: 507 hits
CiteExportLink to record
Permanent link

Direct link
Cite
Citation style
  • apa
  • ieee
  • modern-language-association-8th-edition
  • vancouver
  • Other style
More styles
Language
  • de-DE
  • en-GB
  • en-US
  • fi-FI
  • nn-NO
  • nn-NB
  • sv-SE
  • Other locale
More languages
Output format
  • html
  • text
  • asciidoc
  • rtf