homogenisation heat treatments. The hot ductility deteriorated significantly after long-dwell homogenisation heat treatments for 24 h at temperatures of 1120 and 1190 °C as compared with those treated at a short dwell time of 4 h at the same temperatures. The observed ductility deterioration was related to more extensive liquation along the grain boundaries caused by different mechanisms, e.g., liquation by solute segregation mechanism, Laves melting, constitutional liquation of MC carbides and supersolidus grain boundary melting, with the effect and extent depending on the solute changes after the homogenisation heat treatments. Furthermore, the role of Nb as the solute element and as the precipitate former, as well as the effect of minor alloying elements segregating along the grain boundaries, is discussed in connection to grain boundary liquation, which contributes to a better understanding of heat-affected zone liquation cracking susceptibility of cast ATI® 718Plus®. © 2020 The Authors