Integrity of detonation sprayed CrxCy-NiCr coating under exposure to thermal cycling
2006 (engelsk)Inngår i: Advances in Applied Ceramics: Structural, Functional and Bioceramics, ISSN 1743-6753, E-ISSN 1743-6761, Vol. 105, nr 3, s. 148-152Artikkel i tidsskrift (Fagfellevurdert) Published
Abstract [en]

CrxCy-NiCr coatings with thickness in the range 200-250 mu m were deposited by detonation spray coating on a nickel base superalloy (IN718) substrate and subjected to thermal cycling. Each thermal cycle involved heating to 650 degrees C, the creep temperature of the IN718 substrate, followed by a dwell and then natural cooling to ambient temperature. With thermal cycling, the bulk of the coatings experienced preferential oxidation along the splat boundaries, contributing to an increase in porosity and cracking. Despite the development of porosity and cracks, no spallation of coatings was observed even after nearly 600 thermal cycles. The microhardness of coatings did not undergo significant change, owing to oxide formation and retention of the total carbide content of Cr3C2, Cr7C3 and Cr23C6. The wear behaviour of the as sprayed and thermally cycled coated samples was evaluated in abrasive and erosive wear modes. Wear measurements on as sprayed and thermally cycled coatings showed virtually no deterioration in properties even after exposure to nearly 600 thermal cycles.

sted, utgiver, år, opplag, sider
2006. Vol. 105, nr 3, s. 148-152
Emneord [en]
abrasive wear, chromium carbide, detonation spray coating, erosive wear, thermal cycling, RESISTANCE, CARBIDE, EROSION, Materials Science, Ceramics
Identifikatorer
URN: urn:nbn:se:hv:diva-8444OAI: oai:DiVA.org:hv-8444DiVA, id: diva2:860134
Tilgjengelig fra: 2015-10-10 Laget: 2015-10-08 Sist oppdatert: 2017-12-01bibliografisk kontrollert

Open Access i DiVA

Fulltekst mangler i DiVA

Personposter BETA

Joshi, S. V.

Søk i DiVA

Av forfatter/redaktør
Joshi, S. V.
I samme tidsskrift
Advances in Applied Ceramics: Structural, Functional and Bioceramics

Søk utenfor DiVA

GoogleGoogle Scholar

urn-nbn

Altmetric

urn-nbn
Totalt: 67 treff
RefereraExporteraLink to record
Permanent link

Direct link
Referera
Referensformat
  • apa
  • ieee
  • modern-language-association-8th-edition
  • vancouver
  • Annet format
Fler format
Språk
  • de-DE
  • en-GB
  • en-US
  • fi-FI
  • nn-NO
  • nn-NB
  • sv-SE
  • Annet språk
Fler språk
Utmatningsformat
  • html
  • text
  • asciidoc
  • rtf