Effect of HVAF sprayed NiCoCrAlY coating on oxidation performance of E B PBF manufactured Alloy 718
Högskolan Väst, Institutionen för ingenjörsvetenskap, Avdelningen för avverkande och additativa tillverkningsprocesser (AAT).
2019 (engelsk)Independent thesis Advanced level (degree of Master (One Year)), 10 poäng / 15 hpOppgaveAlternativ tittel
Effekten av HVAF-pålagd NiCoCrAlY beläggning på oxidationsprestandan hos EB-PBF tillverkat Alloy 718 (svensk)
Abstract [en]

There is an upsurge of research interest on Alloy 718 additively manufactured (AM) by electron beam powder bed fusion (EB-PBF) technique in aero and land-based gas turbine engines. However, the surface quality hence the oxidation performance of the manufactured components is of great concern. Along with surface roughness resulted from partially melted powder particles, surface defects such as balls, satellites, microcracks as well as up-skin and down-skin surfaces can enhance the vulnerability of the manufactured parts to oxidation. When the surface is unable to withstand the exposed environment adequately, oxidation can be triggered. The surface-induced failures are increasingly becoming more challenging as the AM components often have complex geometries that render them even more difficult to finish. So, the relatively poor surface finish is the barrier to the full exploitation of the AM industry.

In the present study, a NiCoCrAlY coating deposited by high velocity air-fuel (HVAF) technique on EB-PBF manufactured Alloy 718 was investigated. The oxidation behavior of the parts was investigated in an ambient air environment at 650 and 800 °C for 168 h. The oxidation behavior of the coated samples was analyzed by scanning electron microscopy (SEM) equipped with energy disperse spectroscopy (EDS). The oxidation behavior of the parts was significantly improved after deposition of the thermal spray coating. The oxide scale formed on the surface of the EB-PBF Alloy 718 without the coating was rich in Cr and the oxide scale formed on the surface of the EB-PBF Alloy 718 with NiCoCrAlY coating was rich in Al.

sted, utgiver, år, opplag, sider
2019. , s. 21
Emneord [en]
Additive manufacturing, thermal spray coating, oxidation protection, surface defects, hot isostatic pressing
Emneord [sv]
Additiv tillverkning, termisk sprutning, oxidationsskydd, ytdefekter, het isostatisk pressning
HSV kategori
Identifikatorer
URN: urn:nbn:se:hv:diva-14669Lokal ID: EXP800OAI: oai:DiVA.org:hv-14669DiVA, id: diva2:1366804
Fag / kurs
Mechanical engineering
Utdanningsprogram
Produktionsteknik, magister
Veileder
Examiner
Tilgjengelig fra: 2019-10-31 Laget: 2019-10-30 Sist oppdatert: 2019-10-31bibliografisk kontrollert

Open Access i DiVA

Fulltekst mangler i DiVA

Av organisasjonen

Søk utenfor DiVA

GoogleGoogle Scholar

urn-nbn

Altmetric

urn-nbn
Totalt: 82 treff
RefereraExporteraLink to record
Permanent link

Direct link
Referera
Referensformat
  • apa
  • ieee
  • modern-language-association-8th-edition
  • vancouver
  • Annet format
Fler format
Språk
  • de-DE
  • en-GB
  • en-US
  • fi-FI
  • nn-NO
  • nn-NB
  • sv-SE
  • Annet språk
Fler språk
Utmatningsformat
  • html
  • text
  • asciidoc
  • rtf