Effect of Powder Recycling on the Fracture Behavior of Electron Beam Melted Alloy 718
Chalmers University of Technology, Department of Industrial and Materials Science, Division of Materials and Manufacture, Gothenburg, SE-412 96, Sweden.
Högskolan Väst, Institutionen för ingenjörsvetenskap, Avdelningen för avverkande och additativa tillverkningsprocesser (AAT). (PTW)ORCID-id: 0000-0001-6610-1486
Chalmers University of Technology, Department of Industrial and Materials Science, Division of Materials and Manufacture, Gothenburg, SE-412 96, Sweden.
Chalmers University of Technology, Department of Industrial and Materials Science, Division of Materials and Manufacture, Gothenburg, SE-412 96, Sweden.
2018 (Engelska)Ingår i: Powder Metallurgy Progress, ISSN 1335-8987, Vol. 18, nr 1, s. 40-48Artikel i tidskrift (Övrigt vetenskapligt) Published
Abstract [en]

Understanding the effect of powder feedstock alterations during multicycle additive manufacturing on the quality of built components is crucial to meet the requirements on critical parts for aerospace engine applications. In this study, powder recycling of Alloy 718 during electron beam melting was studied to understand its influence on fracture behavior of Charpy impact test bars. High resolution scanning electron microscopy was employed for fracture surface analysis on test bars produced from virgin and recycled powder. For all investigated samples, an intergranular type of fracture, initiated by non-metallic phases and bonding defects, was typically observed in the regions close to or within the contour zone. The fracture mode in the bulk of the samples was mainly moderately ductile dimple fracture. The results show a clear correlation between powder degradation during multi-cycle powder reuse and the amount of damage relevant defects observed on the fracture surfaces. In particular, samples produced from recycled powder show a significant amount of aluminum-rich oxide defects, originating from aluminum-rich oxide particulates on the surface of the recycled powder. © 2018 H. Gruber et al., published by Sciendo.

Ort, förlag, år, upplaga, sidor
de Gruyter , 2018. Vol. 18, nr 1, s. 40-48
Nyckelord [en]
additive manufacturing of Alloy 718, electron beam melting, powder recycling, powder degradation, fractography of AM components
Nationell ämneskategori
Bearbetnings-, yt- och fogningsteknik
Forskningsämne
TEKNIK, Produktions- och materialteknik; Produktionsteknik
Identifikatorer
URN: urn:nbn:se:hv:diva-12906DOI: 10.1515/pmp-2018-0005Scopus ID: 2-s2.0-85051985288OAI: oai:DiVA.org:hv-12906DiVA, id: diva2:1251462
Forskningsfinansiär
Vinnova
Anmärkning

Funders:  SIP LIGHTer; AoA Production at Chalmers.

Tillgänglig från: 2018-09-27 Skapad: 2018-09-27 Senast uppdaterad: 2019-05-27Bibliografiskt granskad

Open Access i DiVA

Fulltext saknas i DiVA

Övriga länkar

Förlagets fulltextScopus

Personposter BETA

Karimi Neghlani, Paria

Sök vidare i DiVA

Av författaren/redaktören
Karimi Neghlani, Paria
Av organisationen
Avdelningen för avverkande och additativa tillverkningsprocesser (AAT)
Bearbetnings-, yt- och fogningsteknik

Sök vidare utanför DiVA

GoogleGoogle Scholar

doi
urn-nbn

Altmetricpoäng

doi
urn-nbn
Totalt: 31 träffar
RefereraExporteraLänk till posten
Permanent länk

Direktlänk
Referera
Referensformat
  • apa
  • ieee
  • modern-language-association-8th-edition
  • vancouver
  • Annat format
Fler format
Språk
  • de-DE
  • en-GB
  • en-US
  • fi-FI
  • nn-NO
  • nn-NB
  • sv-SE
  • Annat språk
Fler språk
Utmatningsformat
  • html
  • text
  • asciidoc
  • rtf