The weldability of Waspaloy® and Haynes® 282® have been evaluated using the Varestraint weldability test. The experiments reveal that Waspaloy® has a higher susceptibility to hot cracking compared to Haynes® 282®. This conclusion is supported by increased total crack length (10 mm or more) for Waspaloy® when compared to Haynes® 282® in Varestraint test. The cracking in Haynes® 282® seems to be connected with a secondary phase which presumably can be associated with Ti-Mo based MC-type carbide observed in the fusion zone. Also, a surrounding segregated area is present near this secondary phase as well as along the grain boundaries. Furthermore, micro-Vickers hardness results revealed more or less the same weld metal hardness (260-280 HV) but a difference in the base metal hardness. The weld metal hardness of Waspaloy® was lower than that of the base metal hardness, while Haynes® 282® had a higher hardness in comparison.