Comparison of a new, high precision, energy efficient welding method with the conventional Gas Metal Arc Welding on high carbon steel base metal
Högskolan Väst, Institutionen för ingenjörsvetenskap, Avd för tillverkningsprocesser.
2014 (engelsk)Independent thesis Advanced level (degree of Master (One Year)), 10 poäng / 15 hpOppgaveAlternativ tittel
Jämförelse mellan svetsmetod med låg värmetillförsel och konventionell gasmetallbågsvetsning vid svetsning av högkolhaltigt stål (svensk)
Abstract [en]

CMT+P welding is less susceptible to hot cracking than the MAG welding process due to use of low heat input properties. Solidification cracking was found in all weld specimens that had greater 0.39KJ/mm heat inputs. Cracking occurs because of the contraction stresses generates during cooling. Hydrogen cracking is found in HAZ with low heat input parameters, this type of cracking occurred because of very rapid cooling and therefore not enough time to allow the hydrogen to dissipate from the specimen. To eliminate this type of cracking the experiment could be repeated by adding heating during welding to control and reduce the cooling rate. Due to high carbon content in the steel and very fast cooling the microstructure of the weld is martensitic in the base metal as well as the HAZ. Microstructure in the weld and base metal is martensitic due to high carbon con-tent and rapid cooling. At low heat inputs dilution is less and therefore lower carbon content in weld pool. Better weld appearance and weld quality is achieved with CMT+P welding process than the conventional GMA welding processes because of the new wire movement technology during welding

sted, utgiver, år, opplag, sider
2014. , s. 28
Emneord [en]
Gas Metal Arc Welding
HSV kategori
Identifikatorer
URN: urn:nbn:se:hv:diva-6860Lokal ID: EXP800OAI: oai:DiVA.org:hv-6860DiVA, id: diva2:756354
Fag / kurs
Robotics
Utdanningsprogram
Produktionsteknik
Veileder
Examiner
Tilgjengelig fra: 2014-10-20 Laget: 2014-10-17 Sist oppdatert: 2016-11-21bibliografisk kontrollert

Open Access i DiVA

fulltext(1786 kB)314 nedlastinger
Filinformasjon
Fil FULLTEXT01.pdfFilstørrelse 1786 kBChecksum SHA-512
38f1a81d9779d04028b06ad71a2e12069b271081ad92f8df85b494b3a856738e14c3526769d433d37aafd734e0171223414cef1c0e86a80bd3ca36f4fecaa753
Type fulltextMimetype application/pdf

Av organisasjonen

Søk utenfor DiVA

GoogleGoogle Scholar
Totalt: 314 nedlastinger
Antall nedlastinger er summen av alle nedlastinger av alle fulltekster. Det kan for eksempel være tidligere versjoner som er ikke lenger tilgjengelige

urn-nbn

Altmetric

urn-nbn
Totalt: 266 treff
RefereraExporteraLink to record
Permanent link

Direct link
Referera
Referensformat
  • apa
  • ieee
  • modern-language-association-8th-edition
  • vancouver
  • Annet format
Fler format
Språk
  • de-DE
  • en-GB
  • en-US
  • fi-FI
  • nn-NO
  • nn-NB
  • sv-SE
  • Annet språk
Fler språk
Utmatningsformat
  • html
  • text
  • asciidoc
  • rtf